Closest Equivalent Alloy IS 4522 Closest DIN 17445 ASTM - 297 Gr Micro-Structure Heat Treatment T.S. Kg/mm2 min. Y.S. Kg/mm2 min. Elong-action min.% Applications
- - - HA Ferrite - - - - Good oxidation resistance upto 650oC. Used in oil refining industry.
HRCS
28/4
- - HC - As Cast - - - Good sulphur and oxidation resistance upto 10950C. Minimal load bearing capacity.
HRCS
5/28
Grade 4 - HD Ferrite+
Austenite
- 52.53 24.48 8 Can be used in high sulphur application (avoid at 700o-800oC) upto 1000oC.
HRCS
9/29
Grade 6 - HE Ferrite+
Austenite
- 59.47 28.05 10 More ductile and higher corrosion resistance (avoid at 815o C) upto 1050o C for high S atmosphere.
HRCS
9/19
Grade 5 1.4825 HF Austenite As Cast 50.00 24.00 25 Suitable for applications requiring high strength & corrosion resistance at 650o C to 870o C.
HRCS
12/25
Grade 7 1.4837 HH Austenite As Cast 51.50 25.50 10 Suitable for applications between 9270C and 10930C. Not to be used from 7500C to 8900C and for operations invloving thermal shock & carburizing conditions.
HRCS
12/25
- - HH
Type2
Fully Austenite As Cast 51.50 - 4 Same as HH but with superior creep resistance and reduced ductility. Used from 650o C to 1000o C under constant temperature conditions.
HRCS
15/28
- - HI - - 49.47 24.48 10 Higher corrosion resistance and higher strength at temperature upto 1050oC (avoid 815oC).
HRCS
20/25
Grade 9 1.4848 HK Austenite As Cast 45.90 24.00 10 Suitable for stressed parts working upto 1100oC such as billet skids, heat treating trays & fixtures. Unsuited at 815oC and in operations involving thermal shocks.
HRCS
20/25
- 1.4848 HK40 Austenite As Cast 45.90 24.00 10 Same as HK but with better creep strength.
AISI
314
- - - Austenite Solution Annealed - - - Same as HK but Si increased for greater resistance to carburization.
HRCS
HKNb
- - HK40
Nb
- - - - - -
HRCS
24/24 Nb
- 1.4855 IN519 Austenite As Cast 45.00 23.00 10 Same as HK 40 but with enhanced high temperature resistance upto 1025o C.
HRCS
29/20
Grade 10 - HL Austenite - 45.90 24.48 10 Higher corrosion resistance and higher strength at temperature upto 1100o C (avoid 815oC).
HRCS
25/20
Grade 11 - HN Austenite As Cast 43.50 - 8 Suitable for applications upto 1100o C for furnace parts such as grates, etc. with increased ductility.
HRCS 32/20 Nb - 1.4859 Castalloy 800H Austenite As Cast 45.00 18.00 30 Suitable for manifolds and headers. Service limit upto 980o C with increased ductility.
HRCS
35/25
- - HP Austenite As Cast 45.00 23.00 8 Resistant to both oxidizing and carburizing atmospheres at high temperatures upto 1050o C.
HRCS
35/25 Nb
- 1.4852 HP modified Austenite As Cast 45.00 23.00 8 Same as HP but with enhanced high temperature resistance upto 1100o C. Suitable for reformer ethylene furnace tubes, radiant tubes, etc.
HP-Mo - - - - As Cast - - - -
HRCS
35/15
Grade12 - HT Austenite As Cast 45.90 - 4 Suitable for highly stressed parts upto 1095o C including for carburizing operation. High sulphur gases and thermal shocks are detrimental.
HRCS
39/19
Grade 13 - HU Austenite As Cast 45.90 - 4 Suitable for applications upto 1095o C including for carburizing operations. Can withstand corrosive applications with rapid thermal cycles.
45/30
Nbw
- - - Austenite As Cast - - - Useful for components operating in hot zone of pyrolysis coils and components of Reformer outlet manifold service limit 1150o C
22H - 2.4859 - Austenite As Cast 45.00 24.00 4 Same as HP but with enhanced high temperature resistance upto 1150o C. Suitable for radiant tubes, air injection tubes, reformer tubes and fittings for petrochemical furnaces, tube sheets, tube supports, etc. 
Super 22H - - - Austenite As Cast 45.00 24.00 4 Same as 22H but with enhanced high temperature resistance upto 1180o C.
HRCS
60/12
- - HW Austenite - 42.33 - - Excellent thermal shock resistance and resistance to carburisation up to 1040o C where sulphur is not present.
HRCS
66/17
Grade 14 - HX Austenite As Cast 41.50 - - For severe service applications upto 1150o C where corrosion resistance is required.
Canalloy - - - Austenite - - - - Bushes & sleeves for hot dip galvanizing line.
Canalloy Controlled Manganese - - - Austenite - - - - Bushes & sleeves for hot dip galvanizing line.
UMCO-50 - - - - - - - - Furnace parts in heat-treating furnaces, slag notch rings and tundishes.
Cobalt Alloy 6 - R30006 - - - - - - Wear plates and bars, bushes & sleeves for operation in hot & corrosive atmosphere, where lubrication is impossible, with superior performance. Similar to Stellite
Cobalt Alloy 12 - R30012 - - - - - - Cutting tools and bushes & sleeves operation in hot & corrosive atmosphere, where lubrication is impossible, with superior performance. Similar to Stellite
Cobalt Alloy Special - - - Austenite - - - - For better sliding wear property. Hardness is between 375 to 432 HRB. Similar to Stellite
40 Ni
60 CrNb
R20600 - ASTM
A560 Gr
40/60 Nb
- - - - - -
50 Ni
50 CrNb
- 2.4680 ASTM A560 Gr
50/50 Nb
Austenite As Cast 56.00 35.00 5 Suitable for applications upto 950o C in furnace parts. Can withstand fuel ash corrosion. Good creep strength and good resistance to oxidation and carburization.
60 Ni
40 CrNb
- - ASTM
A560 Gr
60/40 Nb
- As Cast - 77.50 60.00 For heat resisting and elevated temperature corrosion resistance application such as tube hangers.
CY-40
(70Ni15Cr)
- - ASTM
A494 Gr
CY-40
Austenite As Cast 49.50 20.00 30 Frequently used for elevated temperature fittings in conjunction with Inconel. Suitable for boiler feed water plants and where high strength, high resistance to wear, corrosion and oxidation at elevated temperatures is required. Similar to Inconel